Acus-velut Mullite Crystalli Quod Confer Maximum Liquefactum, Minimum Reversible Scelerisque Expansion et praeclara Repugnantia Scelerisque Concursorum Concursorum Mullite
- Corundum mullite
- Summus puritatem mixtam mullite
- Electro conflata mullite
Brevis Descriptio
Fused Mullite 75
| Items | Unitas | Index | Typical | |
| Chemical compositione | Al2O3 | % | 73.00-77.00 | 73.90 |
| SiO'2 | % | 22.00-29.00 | 24.06 | |
| Fe2O3 | % | 0.4 max(Fines 0.5%max) | 0.19 | |
| K2O+Na2O | % | 0.40max | 0.16 | |
| CaO+MgO | % | 0.1%max | 0.05 | |
| Refractio | ℃ | 1850min | ||
| mole densitatis | g/cm*3 | 2.90min | 3.1 | |
| Vitrum tempus content | % | 10max | ||
| 3Al2O3.2SiO2Phase | % | 90min | ||
F-Feded; M-Mullite
Mullite conflatum 70
| Items | Unitas | Index | Typical | |
| Chemical compositione | Al2O3 | % | 69.00-73.00 | 70.33 |
| SiO'2 | % | 26.00-32.00 | 27.45 | |
| Fe2O3 | % | 0.6 max(Fines 0.7%max) | 0.23 | |
| K2O+Na2O | % | 0.50max | 0.28 | |
| CaO+MgO | % | 0.2%max | 0.09 | |
| Refractio | ℃ | 1850min | ||
| mole densitatis | g/cm*3 | 2.90min | 3.08 | |
| Vitrum tempus content | % | 15max | ||
| 3Al2O3.2SiO2Phase | % | 85min | ||
Processus productionis
Mullite conflatum producit processus aluminae Bayer et vicus castitatis altae dum in fornacem electrici arcus super-magnam conicit.
Summam habet crystallorum acusilium mullorum quae altum punctum liquefactum conferunt, humilis expansio scelerisque convertibilis et resistentia optimae inpulsa, deformatio sub onere, et corrosio chemica ad caliditatem.
Applicationem
Late usus est materias rudis ad altum gradum refractionum, sicut strati laterum in fornace vitreo fornax et lateres in fornace calido ventorum in industria ferri.
Etiam in fornacibus Ceramicis et petrochemicis industriae et multis aliis applicationibus adhibetur.
Mullite conflatae multae in aliquet pretium pro coatingis inpulsae suae resistentiae et non-wettabilitatis proprietates suas adhibentur
Features
• Maximum scelerisque stabilitatem
• Minimum convertitur scelerisque expansionem
• Repugnantia scoria impetum in altum temperaturis
• Stabilis compositio chemica
Mullite, quaevis species mineralis rarioris aluminii silicatis constans (3Al2O3·2SiO2). In crudas materias aluminosilicatas accendi formatur et est praecipuum album ceramici, murrinae, et temperaturae insulae et refractoriae materiae. Compositiones, ut mulli, habentes rationem alumina-silicam saltem 3:2 infra 1,810° C (3,290° F, non liquescunt), cum vero inferiori ratione partim ad temperaturas tam humilis quam 1,545° C (2,813° liquescat) F).
Naturalis mullite inventa alba, crystallis elongatis in Insula Mull, Hebrides interior, Scot. Agnita est solum in clausuris argillaceis (clayey) fusis in saxa igneis intrusivis, circumstantia quae altissimas formationis calores suggerit.
Praeter momentum ad ceramicos conventionales, mulli electio facta est materialium structuris et functionis ceramicorum provectis ob eius favorabiles proprietates. Nonnullae proprietates mulli praestantes sunt humiles expansio scelerisque, humilis scelerisque conductivity, excellentes resistentia serpunt, summus temperatura fortitudo, et bonum chemicae stabilitatis. Mechanismus formationis mulli pendet a modo coniunctionis alumina- rum et reactantium silica-continentium. Refertur etiam ad temperiem, qua reactio ducit ad formationem mullorum (mulitisation temperatus). Mullitisation temperaturae nuntiata sunt ab Celsio usque ad plures centum gradus secundum synthesim methodi adhibita differre.