Mmetụta nke mineralizers na njirimara nke ihe ndị a seramiiki

Magnesium aluminum spinel (MgAl2O, MgO · Al2Oor MA) nwere elu okpomọkụ n'ibu Njirimara, magburu onwe peeling iguzogide na corrosion iguzogide. Ọ bụ seramiiki okpomọkụ kachasị ahụkarị na sistemụ Al2O-MgO. Uto ọkacha mmasị nke calcium hexaaluminate (CaAl12O19, CaO · 6AlO ma ọ bụ CA6) kristal ọka n'akụkụ ụgbọ elu basal na-eme ka ọ too n'ime platelet ma ọ bụ morphology agịga, nke nwere ike ime ka ihe ahụ sie ike. Calcium dialuminate (CaAlO ma ọ bụ CaO · 2Al203, CA2) nwere ọnụọgụ dị ala nke mgbasawanye ọkụ. Mgbe CAz jikọtara ya na ihe ndị ọzọ nwere ebe mgbaze dị elu yana ọnụ ọgụgụ dị elu nke mgbasawanye, ọ nwere ike iguzogide mmebi nke ujo okpomọkụ kpatara. Ya mere, MA-CA composites enwetawo nlebara anya dị ukwuu dị ka ụdị ọhụrụ nke elu okpomọkụ ihe dị elu na ụlọ ọrụ okpomọkụ dị elu n'ihi njirimara ya nke CA6 na MA.

N'akwụkwọ a, MA seramiiki, MA-CA2-CA ceramic composites na MA-CA ceramic composites kwadebere site na elu okpomọkụ siri ike-phase sintering, na mmetụta nke mineralizers na Njirimara nke ndị a seramiiki ihe a mụrụ. A tụlere usoro ihe ike nke mineralizers na arụmọrụ nke ceramik, wee nweta nsonaazụ nyocha ndị a:
(1) Nsonaazụ gosiri na nnukwu njupụta na ike mgbanwe nke MA seramiiki ihe ji nwayọọ nwayọọ na-abawanye site na mmụba nke okpomọkụ. Mgbe sintering na 1600 maka 2h na sintering arụmọrụ nke MA seramiiki adịghị mma, na a nnukwu njupụta nke 3. 17g/cm3 na a flexural ike uru nke133. 31MPa. Site na mmụba nke mineralizer Fez03, nnukwu njupụta nke ihe seramiiki MA mụbara nke nta nke nta, na ike mgbanwe na-ebu ụzọ mụbaa wee belata. Mgbe ego mgbakwunye bụ 3wt. %, ike mgbanwe ruru 209. 3MPa kacha.

(2) The arụmọrụ na-adọ mejupụtara nke MA-CA6 seramiiki metụtara urughuru size nke CaCO na a-AlO akụrụngwa, ịdị ọcha nke a- Al2O3, okpomọkụ nke njikọ na ejide oge. Iji obere urughuru size CaCO na elu ịdị ọcha a-AlzO3 dị ka akụrụngwa, mgbe sintering na 1600 ℃ na-ejide maka 2h, na synthesized MA-CA6 seramiiki nwere nnukwu mgbanwe ike. The urughuru size nke CaCO3 na-arụ ọrụ dị mkpa na e guzobere CA-adọ na uto na mmepe nke kristal grains na MA-CA6 seramiiki ihe. N'ebe okpomọkụ dị elu, adịghị ọcha Si na a-Alz0 ga-etolite usoro mmiri mmiri na-adịru nwa oge, nke na-eme ka ọdịdị ọdịdị nke ọka CA6 si na platelet pụta.

(3) A na-enyocha mmetụta nke mineralizers ZnO na Mg (BO2) z na njirimara nke MA-CA composites na usoro ike siri ike. Achọpụtara na (Mg-Zn) AI2O4 ngwọta siri ike na mmiri mmiri nwere boron nke ndị na-emepụta ihe na-emepụta ZnO na Mg (BO2) z na-eme ka ọka nke MA dị ntakịrị na ọdịnaya nke MA na-abawanye. A na-eji akụkụ microcrystalline MA kpuchie akụkụ ndị a dị oke egwu iji mepụta ozu ndị gbasasịrị achụsasị mpaghara, nke na-eduga na mgbanwe nke ọka CA6 ka ọ bụrụ ọka equiaxed, si otú ahụ na-akwalite densification nke MA-CA seramiiki ihe na imeziwanye ike mgbanwe ya.

(4) Site na iji nyocha nke dị ọcha Al2O kama nke a-AlzO, MA-CA2-CA seramiiki mejupụtara sitere na akụrụngwa dị ọcha nke nyocha. A mụrụ mmetụta nke mineralizers SnO₂ na HBO na anụ ahụ na akụrụngwa, microstructure na usoro nhazi nke ihe mejupụtara.

Nsonaazụ na-egosi na ngwọta siri ike na mmiri mmiri na-agafe agafe nke boron na-apụta na ihe seramiiki mgbe agbakwunyere mineralizers SnO2 na H2BO; n'otu n'otu, ọ na-eme ka usoro CA2 gbanwee gaa na CA ma na-eme ka nhazi MA na CA6 dịkwuo elu, si otú a na-eme ka ọrụ seramiiki dịkwuo mma. Usoro dị oke oke nke ngafe Ca mepụtara na-eme ka njikọ dị n'etiti ọka MA na CA6 sie ike, nke na-eme ka akụrụngwa seramiiki dịkwuo mma.