Calcium Aluminate Siminti, Babban Aluminate Siminti A600, A700.G9, CA-70, CA-80
Takaitaccen Bayani
Siffofin
Ƙananan porosity, high sinadaran kwanciyar hankali, high zafin jiki yi, high lalacewa juriya
Cikakken bayani
Yawancin lokaci ana amfani da samfurin azaman kayan kiln daban-daban don ƙarfe, petrochemical, man fetur, injiniyoyi, kayan gini da sauran masana'antu.
Babban Simintin Alumina CA-50
| Abubuwa | Naúrar | A600 | A700 | G9 | ||
| Abubuwan sinadaran | Al2O3 | % | 50-60 | 50-60 | 53.5 max | |
| CaO | % | 33 min | 33.00 min | 33.00 min | ||
| SiO2 | % | 8.00 max | 8.00 max | 5.50 max | ||
| Fe2O3 | % | 2.50 max | 2.50 max | 2.50 max | ||
| RO2 | % | 0.4 max | 0.40 max | 0.40 max | ||
| Specific Surface Aea | cm3/g | 3000 max | 3000 max | 350 min | ||
| Saitin Farko | min | 60 min | 60 min | 90 min | ||
| Ƙarshen Saiti | h | 6 max | 6 max | 6 min | ||
| Karfin Lankwasa | kwana 1 | Mpa | 5.50 max | 7.00 min | 8.00 min | |
| kwana 3 | Mpa | 6.50 max | 8.00 min | 10.00 min | ||
| Ƙarfin Ƙarfi | kwana 1 | Mpa | 40.00 max | 50.00 min | 72.00 min | |
| kwana 3 | Mpa | 50.00 max | 60.00 min | 82.00 min | ||
| Refractories | ℃ | 1350 | 1350 | 1450 | ||
Calcium Alumina Cement
| Abubuwa | Naúrar | CA-70 | CA-80 | ||
| Abubuwan sinadaran | Al2O3 | % | 68.50-72.00 | 78.50-81.00 | |
| CaO | % | 28.0-31.50 | 17.00-20.00 | ||
| SiO2 | % | ≤0.50 | ≤0.40 | ||
| Fe2O3 | % | ≤0.50 | ≤0.30 | ||
| K2O+Na2O | % | ≤0.50 | |||
| Specific Surface Aea | Cm2/g | ≥5000 | ≥7000 | ||
| Saitin Farko | min | ≥45 | ≥30 | ||
| Ƙarshen Saiti | h | ≤6 | ≤6 | ||
| Lankwasawa Ƙarfin | 24h ku | Mpa | ≥7.0 | ≥5.50 | |
| M Ƙarfi | 24h ku | Mpa | ≥45 | ≥40 | |
| Refractories | ℃ | ≥ 1600 | ≥1790 | ||